11104400-35 WEICON Stainless Steel Spray Bright Grade

Stainless Steel Spray bright grade

Technical Datasheet

Provides a treated stainless steel look e.g. V2A, V4A
WEICON Stainless Steel Spray „bright grade“is a chemical, corrosion and weather resistant surface coating on the basis of acrylic resin and stainless steel pigments. It is temperature resistant up to +300°C for short periods and provides a treated stainless steel look.

Stainless Steel Spray „bright grade“ can be used wherever a resistant and effective protective layer is required. The alloy is comprised of e.g. chromium, nickel and manganese.

WEICON Stainless Steel Spray „bright grade“ can be used to repair damaged stainless steel parts on truck bodies, silos and pipelines, and in outdoor applications. It can also be used for decorative purposes and for the optical refinement of glass, wood, stone, ceramics and most plastics.

Technical data Colour Stainless steel metallic bright, approx. RAL 9006

Application indoor and outdoor
Binding agent Alkyd resin
Pigment Stainless steel and aluminium pigments
Pigment purity VA-alloy approx. 98,5%
Percentage of metal in dry film approx. 35,0% VA/Al  %
Content 400 ml
Specific weight 0,95 – 1,00 g/cm³
Recommended primer Zinc Spray
Processing temperature +5 up to +35 °C
Consumption at 1.5 cross coats approx. 120 ml/m²
Layer thickness at 1.5 cross coats approx. 15 – 25 µm
dust dry after 10 Min.
Hardened after 10 h
paintable 8 h
Abrasion-resistant yes
Cross cutting  DIN 53151 / ISO 2409 Gt 0 to Gt 1
Salt spraying test ISO 9227 >140 h
Mandrel bend test DIN EN ISO 1519 no hair cracking
Top coating not required
Temperature resistance after complete hardening -50 up to +300 °C
Storage stability 24 months
Pretreatment of the surface Clean and degrease surfaces with WEICON Cleaner S.
Processing Shake can before use till the mixing ball can be heard. Spray on evenly and crosswise at room temperature (approx. +20°C (+68°F)) and at about 25 cm distance from the surface crosswise. Dust-dry after approx. 15 minutes, fully hardened after 10-12 hours.
Storage Pressurized container: protect from sunlight and do not expose to temperatures exceeding +50°C.